Effect of strain rate on microstructure of a low carbon steel wire

Abstract EN

The commercial importance of low alloy carbon steels is due to their plastic deformation properties.

These properties allow them to be formed into useful shapes such as wires.

The present steel is produced by Trifisoud -Setif– Algeria and used for wiring.

It is a low carbon steel wire containing mainly (weight %) 0.05 %C, 0.3 %Mn, 0.1 %S and 0.12 %Cr and is supplied as rods.

The optical microscopic and SEM analyses are used to identify the microstructure of the material in as received and deformed conditions.

It is found that tensile properties depend on the wiredrawing area reduction (τw).

The annealing temperatures and the grain size are determined ; they also vary with τw.

Abstract FRE

L’importance commerciale des aciers au carbone faiblement alliés est du à leurs propriétés de déformation plastique.

Ces propriétés de déformation permettent à ces aciers d’être fabriquer sous forme de fils.

Cette étude concerne un acier destiné au tréfilage, produit par Trifisoud- Setif –Algerie sous forme de barres et contient (%poids) 0.05%C ,0.3%Mn, 0.1%S et 0.12%Cr.

L’analyse par microscopie optique et microscopie électronique à balayage (SEM) est utilisée pour identifier la microstructure du matériau dans les conditions de réception avant et après la déformation.

Il a été mis en évidence que les propriétés mécaniques dépendent du taux de tréfilage (τW).

Les températures de recristallisation et la taille du grain sont déterminées et variaient avec τW.