Flexural behavior of reinforced concrete partially restrained slab specimens subjected to fire flame
Joint Authors
Isa, Mahdi Salih
Habib, Ghalib Muhsin
Husayn, Ali Nasir
Source
The Iraqi Journal for Mechanical and Materials Engineering
Issue
Vol. 2010, Issue B(s) (31 Dec. 2010), pp.211-225, 15 p.
Publisher
University of Babylon College of Engineering
Publication Date
2010-12-31
Country of Publication
Iraq
No. of Pages
15
Main Subjects
Topics
Abstract AR
هذا البحث يعالج سلوك الانثناء للبلاطات الخرسانية المسلحة المقيدة جزئيا من النهايات و المعرضة للحرق بلهب النار.
الدراسة اعتمدت على صب و فحص 16 نموذج مصغر بأبعاد (600*600*40)ملم من البلاطات الخرسانية المسلحة.
تم اختيار خلطتين خرسانية ذات مقاومة انضغاط تصميمية بعمر 28 يوم مقدارها 30 و 38 نيوتن ملم2 و تم اختيار نسبتين لحديد التسليح (0,005 – 0.009).
عرضت النماذج إلى حرارة لهب النار بثلاث مديات (600, 500, 400)درجة سليزية على الوجه السفلي للبلاطة و بزمن تعرض مقداره 1 ساعة, فحصت النماذج لحين الفشل بعد 24 ساعة تحت ثقل موزع منتظم أثناء تقييدها جزئيا ضد الحركة العرضية و الدورانية.
أظهرت النتائج أن مقاومة التحمل الحدية للبلاطات قلت لجميع النماذج المعرضة للهب النار.
كانت المقاومة الحدية المتبقية بعد الحرق في درجة حرارة (400 و 500) أعلى منها في درجة 600 سليزية.
فلقد وجد أنه بعد الحرق بدرجة حرارة 600 سيليزية و لنسبة حديد التسليح (0,005 و 0,009) كانت النسبة المتبقية من المقاومةالحدية تتراوح بين (85 – 87%).
و كانت مقاومة الانضغاط المتبقية عند 600 سيليزية حوالي (63%).
بينما كانت نسبة معايرالتصدع المتبقي يتراوح بين (47 – 51%) أما المتبقي من معايير المرونة فكان يتراوح بين (26 – 29%).
Abstract EN
This research deals with the flexural behavior of partially end restrained slabs subjected to burning by fire flame.
The investigation is based on casting and testing 16 reduced scale (600 × 600 × 40 mm) reinforced concrete slab specimens.
Two concrete mixes with design 28 days compressive strengths of (30 and 38 MPa) were adopted.
Two steel ratios of (0.005, 0.009) were used.
The specimens were exposed to fire flame temperature levels of (400, 500 and 600°C) at the lower surface of the slab specimens with exposure duration of one hour, then after 24 hours ; they were tested in flexure to failure under uniformly distributed load while they are partially edge restrained against lateral and rotational movements.
It was found from the results that the values of ultimate load capacity, decreased for all specimens after exposing to fire flame.
The residual ultimate load capacity for specimens burnt at temperatures of (400 and 500°C) was higher than that for specimens burnt at 600°C.
At temperature around 600°C and for steel ratios of (0.005 and 0.009), the percentages of residual ultimate load ranged between (85 and 87 %) respectively.
The residual compressive strength at 600°C was about (63 %).
However the residual modulus of rupture was in the range of (47 and 51 %) and the residual modulus of elasticity ranged between (29 and 26 %) at 600 ºC.
American Psychological Association (APA)
Isa, Mahdi Salih& Habib, Ghalib Muhsin& Husayn, Ali Nasir. 2010. Flexural behavior of reinforced concrete partially restrained slab specimens subjected to fire flame. The Iraqi Journal for Mechanical and Materials Engineering،Vol. 2010, no. B(s), pp.211-225.
https://search.emarefa.net/detail/BIM-331289
Modern Language Association (MLA)
Isa, Mahdi Salih…[et al.]. Flexural behavior of reinforced concrete partially restrained slab specimens subjected to fire flame. The Iraqi Journal for Mechanical and Materials Engineering No. B (2010), pp.211-225.
https://search.emarefa.net/detail/BIM-331289
American Medical Association (AMA)
Isa, Mahdi Salih& Habib, Ghalib Muhsin& Husayn, Ali Nasir. Flexural behavior of reinforced concrete partially restrained slab specimens subjected to fire flame. The Iraqi Journal for Mechanical and Materials Engineering. 2010. Vol. 2010, no. B(s), pp.211-225.
https://search.emarefa.net/detail/BIM-331289
Data Type
Journal Articles
Language
English
Notes
Includes bibliographical references : p. 223-225
Record ID
BIM-331289