A study of dissolution kinetics of a Nigerian galena ore in hydrochloric acid

Abstract EN

The results of experimental investigation on the study of dissolution kinetics of a Nigerian galena ore in hydrochloric acid solution were discussed.

The influence of acid concentration, temperature, particle size, stirring speed and solid/liquid ratio on the extent of dissolution was examined.

The elemental analysis by XRF showed that the galena ore is composed mainly of PbS with metals such as Sn, Fe and Zn occurring as minor elements and Mn, Rb, Sr and Nb as traces.

The XRD analysis indicated galena as the dominant mineral phase, with the presence of associated minerals, such as a-quartz (SiO2), sphalerite (ZnS), cassiterite (SnO2), pyrite (FeS2) and manganese oxide (MnO2).

Results of leaching studies showed that galena dissolution in HCl solution increases with increasing acid concentration and temperature; while it decreases with particle diameter and solid/liquid ratio at a fixed stirring rate of 450 rpm.

The study showed that 94.8% of galena was dissolved by 8.06 MHCl at 80 °C within 120 min with initial solid/liquid ratio of 10 g/L.

The corresponding activation energy, Ea was calculated to be 38.74 kJ / mol.

Other parameters such as reaction order, Arrhenius constants, reaction and dissociation constants were calculated to be 0.28, 73.69 s_1, 1.73± 0.13 • 103 and 1.37 ± 0.024 • 104 mol L_1 s_1, respectively.

The mechanism of dissolution of galena was established to follow the shrinking core model for the diffusion controlled mechanism with surface chemical reaction as the rate controlling step for the dissolution process.

Finally, the XRD analysis of the postleaching residue showed the presence of elemental sulphur, lead chloride and α-quartz.