Stress Corrosion Cracking of Steel and Aluminum in Sodium Hydroxide : Field Failure and Laboratory Test
Joint Authors
Prawoto, Y.
Sumeru, K.
Wan Nik, W. B.
Source
Advances in Materials Science and Engineering
Issue
Vol. 2012, Issue 2012 (31 Dec. 2012), pp.1-8, 8 p.
Publisher
Hindawi Publishing Corporation
Publication Date
2012-04-08
Country of Publication
Egypt
No. of Pages
8
Main Subjects
Engineering Sciences and Information Technology
Abstract EN
Through an investigation of the field failure analysis and laboratory experiment, a study on (stress corrosion cracking) SCC behavior of steel and aluminum was performed.
All samples were extracted from known operating conditions from the field failures.
Similar but accelerated laboratory test was subsequently conducted in such a way as to mimic the field failures.
The crack depth and behavior of the SCC were then analyzed after the laboratory test and the mechanism of stress corrosion cracking was studied.
The results show that for the same given stress relative to ultimate tensile strength, the susceptibility to SCC is greatly influenced by heat treatment.
Furthermore, it was also concluded that when expressed relative to the (ultimate tensile strength) UTS, aluminum has similar level of SCC susceptibility to that of steel, although with respect to the same absolute value of applied stress, aluminum is more susceptible to SCC in sodium hydroxide environment than steel.
American Psychological Association (APA)
Prawoto, Y.& Sumeru, K.& Wan Nik, W. B.. 2012. Stress Corrosion Cracking of Steel and Aluminum in Sodium Hydroxide : Field Failure and Laboratory Test. Advances in Materials Science and Engineering،Vol. 2012, no. 2012, pp.1-8.
https://search.emarefa.net/detail/BIM-456027
Modern Language Association (MLA)
Prawoto, Y.…[et al.]. Stress Corrosion Cracking of Steel and Aluminum in Sodium Hydroxide : Field Failure and Laboratory Test. Advances in Materials Science and Engineering No. 2012 (2012), pp.1-8.
https://search.emarefa.net/detail/BIM-456027
American Medical Association (AMA)
Prawoto, Y.& Sumeru, K.& Wan Nik, W. B.. Stress Corrosion Cracking of Steel and Aluminum in Sodium Hydroxide : Field Failure and Laboratory Test. Advances in Materials Science and Engineering. 2012. Vol. 2012, no. 2012, pp.1-8.
https://search.emarefa.net/detail/BIM-456027
Data Type
Journal Articles
Language
English
Notes
Includes bibliographical references
Record ID
BIM-456027