Studies on the Potential of Waste Soda Lime Silica Glass in Glass Ionomer Cement Production
Joint Authors
Matori, K. A.
Zainuddin, Norhazlin
Francis Thoo, V. W.
Abdullah, S. A.
Source
Advances in Materials Science and Engineering
Issue
Vol. 2013, Issue 2013 (31 Dec. 2013), pp.1-6, 6 p.
Publisher
Hindawi Publishing Corporation
Publication Date
2013-11-13
Country of Publication
Egypt
No. of Pages
6
Main Subjects
Engineering Sciences and Information Technology
Abstract EN
Glass ionomer cements (GIC) are produced through acid base reaction between calcium-fluoroaluminosilicate glass powder and polyacrylic acid (PAA).
Soda lime silica glasses (SLS), mainly composed of silica (SiO2), have been utilized in this study as the source of SiO2 for synthesis of Ca-fluoroaluminosilicate glass.
Therefore, the main objective of this study was to investigate the potential of SLS waste glass in producing GIC.
Two glasses, GWX 1 (analytical grade SiO2) and GWX 2 (replacing SiO2 with waste SLS), were synthesized and then characterized using X-ray diffraction (XRD) and energy dispersive X-ray (EDX).
Synthesized glasses were then used to produce GIC, in which the properties were characterized using Fourier transform infrared spectroscopy (FT-IR) and compressive test (from 1 to 28 days).
XRD results showed that amorphous glass was produced by using SLS waste glass (GWX 2), which is similar to glass produced using analytical grade SiO2 (GWX 1).
Results from FT-IR showed that the setting reaction of GWX 2 cements is slower compared to cement GWX 1.
Compressive strengths for GWX 1 cements reached up to 76 MPa at 28 days, whereas GWX 2 cements showed a slightly higher value, which is 80 MPa.
American Psychological Association (APA)
Francis Thoo, V. W.& Zainuddin, Norhazlin& Matori, K. A.& Abdullah, S. A.. 2013. Studies on the Potential of Waste Soda Lime Silica Glass in Glass Ionomer Cement Production. Advances in Materials Science and Engineering،Vol. 2013, no. 2013, pp.1-6.
https://search.emarefa.net/detail/BIM-468732
Modern Language Association (MLA)
Francis Thoo, V. W.…[et al.]. Studies on the Potential of Waste Soda Lime Silica Glass in Glass Ionomer Cement Production. Advances in Materials Science and Engineering No. 2013 (2013), pp.1-6.
https://search.emarefa.net/detail/BIM-468732
American Medical Association (AMA)
Francis Thoo, V. W.& Zainuddin, Norhazlin& Matori, K. A.& Abdullah, S. A.. Studies on the Potential of Waste Soda Lime Silica Glass in Glass Ionomer Cement Production. Advances in Materials Science and Engineering. 2013. Vol. 2013, no. 2013, pp.1-6.
https://search.emarefa.net/detail/BIM-468732
Data Type
Journal Articles
Language
English
Notes
Includes bibliographical references
Record ID
BIM-468732