Corrosion Inhibition of Aluminium in HCl by Amine Modified Epoxy Resin
Joint Authors
Otikor, Samuel
Oki, Makanjuola
Oki, Kayode
Otaigbe, John
Source
Issue
Vol. 2013, Issue 2013 (31 Dec. 2013), pp.1-5, 5 p.
Publisher
Hindawi Publishing Corporation
Publication Date
2013-03-05
Country of Publication
Egypt
No. of Pages
5
Main Subjects
Materials Science , Minerals
Civil Engineering
Abstract EN
N-Butyl amine has been grafted unto Dow epoxy resin.
The product was evaluated as an acid inhibitor by gravimetric techniques.
The reduction in corrosion of aluminium in 1 M HCl solution was 92% at 30∘C and 83% at 60∘C with an inhibitor concentration of 100 ppm.
The corrosion rate at this concentration was 3.0×10−2 and 1.5×10−1 mm/yr at 30∘ and 60∘C.
For the specimens in HCl without inhibitor at 10-hour immersion period, the corrosion rate was 3.8×10−1 and 8.6×10−1 mm/yr, respectively, at 30∘ and 60∘C.
Data obtained correlate with Langmuir isotherm.
American Psychological Association (APA)
Oki, Makanjuola& Oki, Kayode& Otaigbe, John& Otikor, Samuel. 2013. Corrosion Inhibition of Aluminium in HCl by Amine Modified Epoxy Resin. Journal of Materials،Vol. 2013, no. 2013, pp.1-5.
https://search.emarefa.net/detail/BIM-474841
Modern Language Association (MLA)
Oki, Makanjuola…[et al.]. Corrosion Inhibition of Aluminium in HCl by Amine Modified Epoxy Resin. Journal of Materials No. 2013 (2013), pp.1-5.
https://search.emarefa.net/detail/BIM-474841
American Medical Association (AMA)
Oki, Makanjuola& Oki, Kayode& Otaigbe, John& Otikor, Samuel. Corrosion Inhibition of Aluminium in HCl by Amine Modified Epoxy Resin. Journal of Materials. 2013. Vol. 2013, no. 2013, pp.1-5.
https://search.emarefa.net/detail/BIM-474841
Data Type
Journal Articles
Language
English
Notes
Includes bibliographical references
Record ID
BIM-474841