Kinetics Study of Photocatalytic Activity of Flame-Made Unloaded and Fe-Loaded CeO2 Nanoparticles

Abstract EN

Unloaded CeO2 and nominal 0.50, 1.00, 1.50, 2.00, 5.00, and 10.00 mol% Fe-loaded CeO2 nanoparticles were synthesized by flame spray pyrolysis (FSP).

The samples were characterized to obtain structure-activity relation by X-ray diffraction (XRD), high-resolution transmission electron microscopy (HRTEM), Brunauer, Emmett, and Teller (BET) nitrogen adsorption, X-ray photoelectron spectroscopy (XPS), and UV-visible diffuse reflectance spectrophotometry (UV-vis DRS).

XRD results indicated that phase structures of Fe-loaded CeO2 nanoparticles were the mixture of CeO2 and Fe2O3 phases at high iron loading concentrations.

HRTEM images showed the significant change in morphology from cubic to almost-spherical shape observed at high iron loading concentration.

Increased specific surface area with increasing iron content was also observed.

The results from UV-visible reflectance spectra clearly showed the shift of absorption edge towards longer visible region upon loading CeO2 with iron.

Photocatalytic studies showed that Fe-loaded CeO2 sample exhibited higher activity than unloaded CeO2, with optimal 2.00 mol% of iron loading concentration being the most active catalyst.

Results from XPS analysis suggested that iron in the Fe3+ state might be an active species responsible for enhanced photocatalytic activities observed in this study.