Intense Red Upconversion Emission and Shape Controlled Synthesis of Gd2O3 : YbEr Nanocrystals

Abstract EN

Yb/Er codoped Gd(OH)3 was synthesized firstly via a simple hydrothermal treatment of the corresponding nitrate in the presence of alkali by tuning the pH values.

The Gd2O3:Yb/Er nanocrystals were obtained via sintering the corresponding hydroxides precursors.

The as-prepared samples were characterized by the typical X-ray diffraction, energy-dispersive X-ray spectroscopy, transmission electron microscopy (TEM), high-resolution TEM, and spectrophotometer.

The results revealed that two shapes of the as-prepared Gd2O3:Yb/Er nanocrystals can be readily tuned from lemon-like particle to rod-like structure via tuning pH values from 7 to 14.

Moreover, compared with the samples prepared at pH 7, the Gd2O3:Yb/Er nanocrystals prepared at pH 14 exhibit enhanced red upconversion emission and higher upconversion luminescence intensity under the excitation of 980 nm laser.