Electrochemical Impedance Study of Zinc Yellow Polypropylene-Coated Aluminum Alloy
Joint Authors
Lu, Feng
Cai, Jian-ping
Liu, Ming
Zhang, Ni
Sun, Zhi-hua
Source
International Journal of Corrosion
Issue
Vol. 2010, Issue 2010 (31 Dec. 2010), pp.1-6, 6 p.
Publisher
Hindawi Publishing Corporation
Publication Date
2010-03-08
Country of Publication
Egypt
No. of Pages
6
Main Subjects
Abstract EN
Performance of zinc yellow polypropylene-coated aluminum alloy 7B04 during accelerated degradation test is studied using electrochemical impedance spectroscopy (EIS).
It has been found that the zinc yellow polypropylene paint has few flaw and acts as a pure capacitance before accelerated test.
After 336-hour exposure to the test, the impedance spectroscopy shows two time constants, and water has reached to the aluminum alloy/paint interface and forms corrosive microcell.
For the scratched samples, the reaction of metal corrosion and the hydrolysis of zinc yellow ion can occur simultaneously.
The impedance spectroscopy indicates inductance after 1008-hour exposure to the test, but the inductance disappears after 1344-hour exposure and the passivation film has pitting corrosion.
American Psychological Association (APA)
Sun, Zhi-hua& Cai, Jian-ping& Liu, Ming& Lu, Feng& Zhang, Ni. 2010. Electrochemical Impedance Study of Zinc Yellow Polypropylene-Coated Aluminum Alloy. International Journal of Corrosion،Vol. 2010, no. 2010, pp.1-6.
https://search.emarefa.net/detail/BIM-478912
Modern Language Association (MLA)
Sun, Zhi-hua…[et al.]. Electrochemical Impedance Study of Zinc Yellow Polypropylene-Coated Aluminum Alloy. International Journal of Corrosion No. 2010 (2010), pp.1-6.
https://search.emarefa.net/detail/BIM-478912
American Medical Association (AMA)
Sun, Zhi-hua& Cai, Jian-ping& Liu, Ming& Lu, Feng& Zhang, Ni. Electrochemical Impedance Study of Zinc Yellow Polypropylene-Coated Aluminum Alloy. International Journal of Corrosion. 2010. Vol. 2010, no. 2010, pp.1-6.
https://search.emarefa.net/detail/BIM-478912
Data Type
Journal Articles
Language
English
Notes
Includes bibliographical references
Record ID
BIM-478912