Critical Analysis on the Structural and Magnetic Properties of Bulk and Nanocrystalline Cu-Fe-O

Abstract EN

Nanocrystalline and bulk samples of “Fe”-doped CuO were prepared by coprecipitation and ceramic methods.

Structural and compositional analyses were performed using X-ray diffraction, SEM, and EDAX.

Traces of secondary phases such as CuFe2O4, Fe3O4, and α-Fe2O3 having peaks very close to that of the host CuO were identified from the Rietveld profile analysis and the SAED pattern of bulk and nanocrystalline Cu0.98Fe0.02O samples.

Vibrating Sample Magnetometer (VSM) measurements show hysteresis at 300 K for all the samples.

The ferrimagnetic Neel transition temperature (TN) was found to be around 465°C irrespective of the content of “Fe”, which is close to the TN value of cubic CuFe2O4.

High-pressure X-Ray diffraction studies were performed on 2% “Fe”-doped bulk CuO using synchrotron radiation.

From the absence of any strong new peaks at high pressure, it is evident that the secondary phases if present could be less than the level of detection.

Cu2O, which is diamagnetic by nature, was also doped with 1% of “Fe” and was found to show paramagnetic behavior in contrast to the “Fe” doped CuO.

Hence the possibility of intrinsic magnetization of “Fe”-doped CuO apart from the secondary phases is discussed based on the magnetization and charge state of “Fe” and the host into which it is substituted.