Effect of Dentin Biomodification Using Naturally Derived Collagen Cross-Linkers : One-Year Bond Strength Study

Abstract EN

Purpose.

This study investigated the long-term resin-dentin bond strength of dentin biomodified by proanthocyanidin-rich (PA) agents.

Materials and Methods.

Forty molars had their coronal dentin exposed, etched, and treated for 10 minutes with 6.5% grape seed extract (GSE), 6.5% cocoa seed extract ethanol-water (CSE-ET), 6.5% cocoa seed extract acetone-water (CSE-AC), and distilled water (CO).

Samples were restored either with One-Step Plus (OS) or Adper Single-Bond Plus (SB).

Bond strength test was performed immediately or after 3, 6, and 12 months.

Results.

Higher μTBS were observed for GSE immediately (SB- 62.9 MPa; OS- 51.9 MPa) when compared to CSE-ET (SB- 56.95 MPa; OS- 60.28 MPa), CSE-AC (SB- 49.97 MPa; OS- 54.44 MPa), and CO (SB- 52.0 MPa; OS- 44.0 MPa) (P<0.05).

CSE outcomes were adhesive system and solvent dependant.

After 12 months storage SB results showed no difference among treatment types (GSE- 57.15 MPa; CSE/ET- 54.04 MPa; CSE/AC- 48.22 MPa; CO- 51.68 MPa; P=0.347),while OS results where treatment dependent (GSE- 42.62 MPa; CSE/ET- 44.06 MPa; CSE/AC- 41.30 MPa; CO- 36.85 MPa; P=0.036).

Conclusions.

GSE and CSE-ET agents provided enhanced immediate adhesion and stabilization to demineralized dentin after long-term storage, depending on adhesive system.