CdSe Quantum Dots for Solar Cell Devices

Abstract EN

CdSe quantum dots have been prepared with different sizes and exploited as inorganic dye to sensitize a wide bandgap TiO2 thin films for QDs solar cells.

The synthesis is based on the pyrolysis of organometallic reagents by injection into a hot coordinating solvent.

This provides temporally discrete nucleation and permits controlled growth of macroscopic quantities of nanocrystallites.

XRD, HRTEM, UV-visible, and PL were used to characterize the synthesized quantum dots.

The results showed CdSe quantum dots with sizes ranging from 3 nm to 6 nm which enabled the control of the optical properties and consequently the solar cell performance.

Solar cell of 0.08% performance under solar irradiation with a light intensity of 100 mW/cm2 has been obtained.

CdSe/TiO2 solar cells without and with using mercaptopropionic acid (MPA) as a linker between CdSe and TiO2 particles despite a Voc of 428 mV, Jsc of 0.184 mAcm-2, FF of 0.57, and η of 0.05% but with linker despite a Voc of 543 mV, Jsc of 0.318 mAcm-2 , FF of 0.48, and η of 0.08%, respectively.