Study of the influence of surface roughness, sample heat and sample shape onwear rate measurements
Other Title(s)
دراسة تأثير خشونة السطح، درجة حرارة النموذج و شكل النموذج على قياسات معدل البلى
Joint Authors
Judran, Abd al-Hadi k.
Kazim, Najim
Husayn, Haytham T.
Source
Engineering and Technology Journal
Issue
Vol. 31, Issue 2B (28 Feb. 2013), pp.252-260, 9 p.
Publisher
Publication Date
2013-02-28
Country of Publication
Iraq
No. of Pages
9
Main Subjects
Topics
Abstract AR
تم في هذا العمل تحضير و تشغيل نماذج من المعادن كالنحاس و الألمنيوم و نموذج من السبائك كالبراص و تشغيلها كأقراص (نماذج مستوية) و أنصاف حلقات (نماذج منحنية).
تم تنعيم جميع النماذج باستخدام ورق تنعيم بمختلف الدرجات و تم قياس الخشونة المايكروية للسطح لجميع النماذج و كذلك قياس أوزانها الابتدائية و بعدها تم إجراء فحص البلى تحت شرط التزييت و تحت حمل عمودي ثابت مقداره 15 نيوتن و وقت انزلاق 30 دقيقة و سرعة انزلاق 750 دورة / دقيقة.
خلال تشغيل منظومة فحص البلى قيست درجة حرارة النماذج و تم حساب معدل البلى باستخدام الطريقة الوزنية.
و من النتائج التي حصلنا عليها يمكن ملاحظة أن الزيادة في قيم الخشونة المايكروية تؤدي إلى زيادة في الوزن المفقود و معدل البلى و درجة حرارة النماذج.
كذلك فإن تأثير شكل النموذج على الوزن المفقود، معدل البلى و درجة حرارة النماذج يبدو واضحا حيث أظهرت قياسات الوزن المفقود، معدل البلى و درجة حرارة للنماذج المنحنية أنها أعلى من تلك التي قيست للنماذج المستوية.
Abstract EN
Metal samples such as Copper and Aluminum and alloy as Brass were prepared and machined as discs (plane sample) and as a half rings (curvature sample).
The samples were polished by using metallographic paper with different grades.
The micro roughness and the initial weight were measured for all samples before wear tests, and then the samples were subjected to wear testing system under lubricated condition, fixed normal load of 15N, sliding time 30 min and sliding speed of 750 rpm.
During the running of wear testing system the temperature of the samples were measured .The wear rate was calculated by employing the weighing method.
It is clear from the results that micro roughness values increasing leads to increase in weight loss , wear rate and the temperature of samples .The effect of sample shape on weight loss , wear rate and sample heat is also obvious when noticing that the different measurements of weight loss, wear rate and sample heat of curvature samples are higher than that of plane samples .
American Psychological Association (APA)
Judran, Abd al-Hadi k.& Kazim, Najim& Husayn, Haytham T.. 2013. Study of the influence of surface roughness, sample heat and sample shape onwear rate measurements. Engineering and Technology Journal،Vol. 31, no. 2B, pp.252-260.
https://search.emarefa.net/detail/BIM-549560
Modern Language Association (MLA)
Judran, Abd al-Hadi k.…[et al.]. Study of the influence of surface roughness, sample heat and sample shape onwear rate measurements. Engineering and Technology Journal Vol. 31, no. 2B (2013), pp.252-260.
https://search.emarefa.net/detail/BIM-549560
American Medical Association (AMA)
Judran, Abd al-Hadi k.& Kazim, Najim& Husayn, Haytham T.. Study of the influence of surface roughness, sample heat and sample shape onwear rate measurements. Engineering and Technology Journal. 2013. Vol. 31, no. 2B, pp.252-260.