Role of hydroxyl group in cerium hydroxycinnamate on corrosion inhibition of mild steel in 0.6 M NaCl solution

Abstract EN

The corrosion inhibition mechanism of cerium hydroxycinnamate compounds has been studied and compared as an effective corrosion inhibitor for steel in an aqueous 0.6 M NaCl solution.

Surface analysis results showed that the surface of steel coupons exposed to solutions containing cerium hydroxycinnamate compounds has less signs of corrosion attack due to a formation of the protective film, while the surface of mild steel coupons exposed to 0.6 M chloride solution without inhibitor additions was severely corroded due to pitting.

Electrochemical results performed a good inhibition performance and information of the formed protective deposit that hinders the electrochemical corrosion reactions with a dominance of anodic inhibition mechanism.

The results also indicated that the addition of cerium hydroxycinnamate compounds to 0.6 M NaCl solution could mitigate electrochemical corrosion reactions, reduce protective and double layer CPE magnitudes, and improve protective and charge transfer resistances.

Furthermore, cerium 2-hydroxycinnamate showed better efficient corrosion inhibitor in comparison with cerium 4-hydroxycinnamate for steel in aqueous media containing 0.6 M chloride ion.