Improvement of electric and magnetic properties for li spinel ferrite by divalent Ni2+ ions substitution
Other Title(s)
تأثير أيونات النيكل الثنائية على الخواص الكهربية و المغناطيسية لليثيوم أسبنل فيريت
Dissertant
al-Hulw, Ilham Abd al-Fattah Ibrahim
Thesis advisor
University
Islamic University
Faculty
Faculty of Science
Department
Department of Physics
University Country
Palestine (Gaza Strip)
Degree
Master
Degree Date
2017
English Abstract
In the present work magnetic, electric and dielectric properties are investigated for mixed ferrite Li0.5(1-x)NixFe2.5-0.5xO4 ( where x=0.0, 0.2, 0.4, 0.6, 0.8 and 1.0) which are prepared from high purity oxides using standard ceramic technique.
The net magnetization (M) was measured at room temperature in the range of the applied field [200-2650 (A/m)].
The results indicated that the M decreased with increasing of the ions.
The highest value of M was registered for the sample of x=0.0, where the lowest value was registered for the samples of x=1.0.
The inductance was measured as a function of temperature to determine the Curie temperature (It is the temperature which the material transform from ferrimagnetic to paramagnetic .
It was found that, the Curie temperature decreased with increasing of the Ni2+ ions.
Complex dielectric constant ( ), dielectric loss tangent ( ) and AC conductivity ( ) were investigated in the frequency range of at room temperature.
It was found that, the and were decreased continuously, while was increased with increasing of the applied frequency.
Main Subjects
No. of Pages
56
Table of Contents
Table of contents.
Abstract.
Abstract in Arabic.
Chapter One : Theoretical background.
Chapter Two : Literature survey.
Chapter Three : Experimental techniqes.
Chapter Four : Results and discussion.
Conclusion.
References.
American Psychological Association (APA)
al-Hulw, Ilham Abd al-Fattah Ibrahim. (2017). Improvement of electric and magnetic properties for li spinel ferrite by divalent Ni2+ ions substitution. (Master's theses Theses and Dissertations Master). Islamic University, Palestine (Gaza Strip)
https://search.emarefa.net/detail/BIM-902555
Modern Language Association (MLA)
al-Hulw, Ilham Abd al-Fattah Ibrahim. Improvement of electric and magnetic properties for li spinel ferrite by divalent Ni2+ ions substitution. (Master's theses Theses and Dissertations Master). Islamic University. (2017).
https://search.emarefa.net/detail/BIM-902555
American Medical Association (AMA)
al-Hulw, Ilham Abd al-Fattah Ibrahim. (2017). Improvement of electric and magnetic properties for li spinel ferrite by divalent Ni2+ ions substitution. (Master's theses Theses and Dissertations Master). Islamic University, Palestine (Gaza Strip)
https://search.emarefa.net/detail/BIM-902555
Language
English
Data Type
Arab Theses
Record ID
BIM-902555