Synthesis of Silica-Coated Magnetic Nanoparticles and Application in the Detection of Pathogenic Viruses

الملخص EN

Magnetic Fe3O4 nanoparticles were prepared by coprecipitation and then coated with silica.

These Fe3O4/SiO2 nanoparticles consisted of a 10–15 nm magnetic core and a silica shell of 2–5 nm thickness.

The superparamagnetic property of the Fe3O4/SiO2 particles with the magnetization of 42.5 emu/g was confirmed by vibrating sample magnetometer (VSM).

We further optimized buffers with these Fe3O4/SiO2 nanoparticles to isolate genomic DNA of hepatitis virus type B (HBV) and of Epstein-Barr virus (EBV) for detection of the viruses based on polymerase chain reaction (PCR) amplification of a 434 bp fragment of S gene specific for HBV and 250 bp fragment of nuclear antigen encoding gene specific for EBV.

The purification efficiency of DNA of both HBV and EBV using obtained Fe3O4/SiO2 nanoparticles was superior to that obtained with commercialized Fe3O4/SiO2 microparticles, as indicated by (i) brighter PCR-amplified bands for both HBV and EBV and (ii) higher sensitivity in PCR-based detection of EBV load (copies/mL).

The time required for DNA isolation using Fe3O4/SiO2 nanoparticles was significantly reduced as the particles were attracted to magnets more quickly (15–20 s) than the commercialized microparticles (2-3 min).