Effects of Hydrogen on the Optical and Electrical Characteristics of the Sputter-Deposited Al2O3-Doped ZnO Thin Films

الملخص EN

In this study, AZO thin films were deposited on glass by using a 98 mol% ZnO + 1 mol% Al2O3 (AZO, Zn : Al = 98 : 2) ceramic target and a r.f.

magnetron sputtering system.

At first, the effects of different H2 flow rates (H2/(H2 + Ar) = 0%~9.09%, abbreviated as H2-deposited AZO thin films, deposition temperature was 200°C) added during the deposition process on the physical and electrical properties of AZO thin films were investigated.

The optical transmittance at 400 nm~700 nm is more than 80% for all AZO thin films regardless of H2 flow rate and the transparency ratio decreased as the H2 flow rate increased.

The Burstein-Moss shift effect was used to prove that the defects of AZO thin films decreased with increasing H2 flow rate.

Also, the 2% H2-deposited AZO thin films were also treated by the H2 plasma at room temperature for 60 min (plasma-treated AZO thin films).

The value variations in the optical band gap ( E g ) values of the H2-deposited and plasma-treated AZO thin films were evaluated from the plots of α h ν 2 = c ( h ν − E g ) , and the E g values increased with increasing H2 flow rate.

The E g values also increased as the H2-plasma process was used to treat on the H2-deposited Al2O3-doped ZnO (AZO) thin films.