Self-Ordered Voids Formation in SiO2 Matrix by Ge Outdiffusion

الملخص EN

The annealing behavior of very thin SiO2/Ge multilayers deposited on Si substrate by e-gun deposition in high vacuum was explored.

It is shown that, after annealing at moderate temperatures (800°C) in inert atmosphere, Ge is completely outdiffused from the SiO2 matrix leaving small (about 3 nm) spherical voids embedded in the SiO2 matrix.

These voids are very well correlated and formed at distances governed by the preexisting multilayer structure (in vertical direction) and self-organization (in horizontal direction).

The formed films produce intensive photoluminescence (PL) with a peak at 500 nm.

The explored dynamics of the PL decay show the existence of a very rapid process similar to the one found at Ge/SiO2 defected interface layers.