Nanoporous Calcium Silicate and PLGA Biocomposite for Bone Repair

الملخص EN

Nanoporous calcium silicate (n-CS) with high surface area was synthesized using the mixed surfactants of EO20PO70EO20 (polyethylene oxide)20(polypropylene oxide)70(polyethylene oxide)20, P123) and hexadecyltrimethyl ammonium bromide (CTAB) as templates, and its composite with poly(lactic acid-co-glycolic acid) (PLGA) were fabricated.

The results showed that the n-CS/PLGA composite (n-CPC) with 20 wt% n-CS could induce a dense and continuous layer of apatite on its surface after soaking in simulated body fluid (SBF) for 1 week, suggesting the excellent in vitro bioactivity.

The n-CPC could promote cell attachment on its surfaces.

In addition, the proliferation ratio of MG63 cells on n-CPC was significantly higher than PLGA; the results demonstrated that n-CPC had excellent cytocompatibility.

We prepared n-CPC scaffolds that contained open and interconnected macropores ranging in size from 200 to 500 μm.

The n-CPC scaffolds were implanted in femur bone defect of rabbits, and the in vivo biocompatibility and osteogenicity of the scaffolds were investigated.

The results indicated that n-CPC scaffolds exhibited good biocompatibility, degradability, and osteogenesis in vivo.

Collectively, these results suggested that the incorporation of n-CS in PLGA produced biocomposites with improved bioactivity and biocompatibility.